| About |
|---|
| Description Non-flammable PP, FH51 and FH51G, have a feature of high heat-resistance and rigidity, while FH42P can be used for out-door, for example X-Mas socket, needing heat/weathering resistance. To be applied for Out-Door, the required standard is UL of non-flammability and eco-friendly feature. FH42P Grade keeps non-flammability of UL94 V-0 and fl grade of UL746C, while FH51 exhibits excellent non-flammability of UL94 V-2. Characteristics FH51G : As non-flammability of UL94 V-2 grade, it is easy to form with excellent fluidity and widely used for, in particular, extension sockets with its high heat resistance and rigidity. Applications Extension socket needing high heat-resistance and rigidity FH51G)&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,High liquidity,Flame Characteristics,High Heat Resistance,V-2 |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.970 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.2 to 1.5 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 29 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 128 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 104 | ASTM D785 | |
| tensile strength | |||
| yield | 32.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| Bending modulus | 2110 | MPa | ASTM D790 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | UL 94 | |
| 0.75 mm | 120 | ℃ | UL 746B |
| 1.60 mm | 850 | ℃ | IEC 60695-2-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 2.0 | hr | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 180 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Injection pressure | 39.2 to 78.5 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |