| About |
|---|
| Type: Polyether Thermoplastic Polyurethane (TPU) Special Feature: Moisture Vapor Transmission, with Excellent Hydrolysis Resistance, Low Temperature and Wide Process Window Processes: Extrusion: Blown, Flat Die Cast Film, Injection and Cable Jacketing&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Hydrolysis stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 | g/cm³ | ASTM D792 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Water vapor permeability | 450 | g/m²/24 hr | ASTM E96 |
| Water vapor transmittance | |||
| Mocon，38℃，25.4 µm | 1800 | g/m²/24 hr | ASTM D6701 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile permanent deformation | |||
| 200% strain | 11 | % | ASTM D412 |
| tensile strength | ASTM D412 | ||
| Fracture, 0.762 mm | 37.9 | MPa | ASTM D412 |
| 100% strain, 0.762 mm | 4.80 | MPa | ASTM D412 |
| 300% strain, 0.762 mm | 7.60 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 0.762 mm | 650 | % | ASTM D412 |
| tear strength | |||
| 0.762 mm | 69.6 | kN/m | ASTM D624 |
| cracking | 23 | kN/m | ASTM D470 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -50.0 | ℃ | ASTM D3418 |
| Melting temperature | 130 | ℃ | DSC |
| Kofler Melting Temperature | 125 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 82 | ASTM D2240 | |
| Taber abraser | |||
| 1000 cycles, 1000 g, H-18 wheels | 22.0 | mg | ASTM D3389 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 104 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 166 | °C | |
| Barrel 2 zone temperature | 171 | °C | |
| Barrel 3 zone temperature | 177 | °C | |
| Barrel 4 zone temperature | 182 | °C | |
| Connector temperature | 182 | °C | |
| Melt temperature | 179 | °C | |
| Nozzle temperature | 182 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure BW |
| 3. 23°C, 50% RH |
| 4. 90% RH |
| 5. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |