| About |
|---|
| AdSint® PA12 GB30 (Glass Beads) is a nylon based powder filled with glass beads. It offers high stiffness by increasing the tensile modulus with slightly effect on the others mechanical properties. Used for parts requiring high temperature and wear resistance (e.g. housings). Due to its better yield rate per kg it also offers a cost advantage. AdSint® PA12 GB30 has been tested on most common SLS printers. Parameters for printing will be provided. The refresh rate is between 30% and 40%, depending on the application.&& |
| Product Description | |
|---|---|
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance,Good wear resistance |
| Availabilitys | Europe |
| Process Methods | 3D Printing, Laser Sintering/Melting |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.10 to 1.20 | g/cm³ | ISO 61 |
| Apparent density | 0.57 to 0.67 | g/cm³ | ISO 1068 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.30 to 0.50 | % | ISO 62 |
| Particle size distribution | |||
| Course Particles <22 µm | < 10 | % | |
| Course Particles >55 µm | < 10 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 37 to 41 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 175 to 185 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 85.0 to 95.0 | ℃ | ISO 75-2/A |
| Glass transition temperature | 40.0 to 44.0 | ℃ | ISO 11357-2 |
| Melting temperature | 180 to 184 | ℃ | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mean Diameter | 35.0 | µm | ISO 13320 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 20 ℃ | 75 to 77 | ISO 868 | |
| Tensile modulus | 2900 to 3100 | MPa | ISO 527-2/1B |
| tensile strength | 31.0 to 33.0 | MPa | ISO 527-2/1B |
| Tensile strain | |||
| fracture | 10 to 12 | % | ISO 527-2/1B |
| Bending modulus | |||
| 23℃ | 2280 to 2330 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Packed |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |