Safron® H510-02

About
Safron® H510-02 Polypropylene Resin is a homopolymer suitable for extrusion, general purpose injection and blow moulding. It offers good processability and low water carry-over, required when water baths are used during processing. Safron® H510-02 Polypropylene Resin offers good tenacity and low fibrillation. Typical Applications Integral hinged closures Stretched tapes for carpet backing and woven products Monofilaments Strapping&&

About

Safron® H510-02 Polypropylene Resin is a homopolymer suitable for extrusion, general purpose injection and blow moulding. It offers good processability and low water carry-over, required when water baths are used during processing. Safron® H510-02 Polypropylene Resin offers good tenacity and low fibrillation. Typical Applications Integral hinged closures Stretched tapes for carpet backing and woven products Monofilaments Strapping&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,Food contact compliance,Low water portability,Homopolymer
Availabilitys	Africa & Middle East
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	2.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, injection molding	31.0	MPa	ISO 527-2
Tensile strain
Yield, injection molding	8.5	%	ISO 527-2
Bending modulus
injection molding	1360	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23 ℃, injection molding	6.8	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	85.0	℃	ISO 75-2/B
1.8 MPa, unannealed	53.0	℃	ISO 75-2/A
Vicat Softening Temp	90.0	℃	ISO 306/B

Supplementary information	Nominal value	Unit
Blow molding mold temperature	220	℃
Blowing molding temperature
Zone	180 to 200	℃
Zone	210 to 230	℃
Zone	230 to 250	℃
Zone	220 to 240	℃

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Barrel rear temperature	190	°C
Barrel middle temperature	220 to 250	°C
Barrel front temperature	240 to 250	°C
Nozzle temperature	240	°C
Barrel 1 zone temperature	190	°C
Barrel 2 zone temperature	215	°C
Barrel 3 zone temperature	240	°C
Barrel 4 zone temperature	250	°C
Nozzle temperature	245	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.