| PC/ASA. Excellent weatherability, low gloss.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ASA+PC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low Gloss |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 260℃，5 kg | 28.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD：3.2 mm | 0.60 to 0.90 | % | Internal Method |
| MD：3.2 mm | 0.60 to 0.90 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2330 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 45.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 47 | % | ISO 527-2/50 |
| yield | 5.2 | % | ISO 527-2/50 |
| Bending modulus | 2270 | MPa | ISO 178 |
| bending strength | 93.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 12 | kJ/m² | ISO 179/1eA |
| -30℃ | 14 | kJ/m² | ISO 179/1eA |
| 23℃ | 25 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 8.0 | kJ/m² | ISO 180-1A |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -30℃，Energy at Peak Load | 15.0 | J | ASTM D3763 |
| -30℃，Total Energy | 17.0 | J | ASTM D3763 |
| 23℃，Energy at Peak Load | 45.0 | J | ASTM D3763 |
| 23℃，Total Energy | 53.7 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 103 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 125 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| B50 | 126 | ℃ | ISO 306 |
| Linear coefficient of thermal expansion | |||
| TD：-30~80℃ | 7.6E-5 | 1/℃ | ISO 11359-2 |
| MD：-30~80℃ | 6.7E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 to 105 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 250 to 275 | °C | |
| Barrel front temperature | 240 to 270 | °C | |
| Nozzle temperature | 260 to 275 | °C | |
| Processing (melt) temperature | 265 to 285 | °C | |
| Mold temperature | 50 to 82 | °C | |
| Back pressure | 0.300 to 1.00 | MPa | |
| Screw speed | 30 to 80 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. Yield |
| 4. 80*10*3 sp=62mm |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 |
| 7. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |