| About |
|---|
| 2235L-75 CLEAR 030X is a 90C rated, unique, extraction resistant flexible vinyl compound with good elasticity, low temperature performance, and excellent color and property retention after irradiation. Component extraction by lipids, polystyrene, polycarbonate or other fatty materials is extremely low. Phthalate free, 2235L-75 CLEAR 030X was designed to meet USP Class VI and cytotoxicity testing for disposable medical devices&& |
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Features | High elastic,Good color stability |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 to 1.25 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shore A, 10 seconds, 3.18 mm | 72 to 78 | ASTM D2240 | |
| Shore A, 15 seconds, 6.35 mm | 70 to 76 | ASTM D2240 | |
| Tensile modulus | |||
| 100% secant, 1.91 mm | 7.34 | MPa | ASTM D638 |
| tensile strength | |||
| 1.91 mm | 19.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 1.91 mm | 330 | % | ASTM D638 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 61.3 | kN/m | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -33.0 | ℃ | ASTM D746 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 149 | °C | |
| Barrel 2 zone temperature | 154 | °C | |
| Barrel 3 zone temperature | 160 | °C | |
| Barrel 4 zone temperature | 166 | °C | |
| Barrel 5 zone temperature | 171 | °C | |
| Connector temperature | 174 | °C | |
| Melt temperature | 171 to 179 | °C | |
| Nozzle temperature | 174 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Graves |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |