| About |
|---|
| High flow, High Heat resistance, Low Warpage, for Thick Walled (>0.2mm) or thin (<0.2mm)& Thick Walled combination parts. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.4mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130°C, mechanicals 130°C. UL = Underwriters Laboratories (USA)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | Low warping,High liquidity,High Heat Resistance,V-0 |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.76 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.20 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 120 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.4 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 12000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 185 | MPa | ISO 178 |
| Fracture bending strain | 2.0 | % | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8.0 MPa, unannealed | 271 | ℃ | ISO 75-2/C |
| 1.8 MPa, unannealed | 315 | ℃ | ISO 75-2/A |
| Melting temperature | 350 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 1.7E-5 | 1/℃ | ISO 11359-2 |
| MD | 8.0E-6 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 7.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 150 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 to 170 | °C | |
| Drying time | 6.0 | hr | |
| Hopper temperature | 20 to 40 | °C | |
| Barrel rear temperature | 330 to 350 | °C | |
| Barrel middle temperature | 340 to 360 | °C | |
| Barrel front temperature | 345 to 365 | °C | |
| Nozzle temperature | 355 to 370 | °C | |
| Processing (melt) temperature | 360 to 375 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 50.0 to 150 | MPa | |
| Injection speed | Moderate | ||
| Hold pressure | 50.0 to 150 | MPa | |
| Back pressure | 0.00 to 3.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |