Borealis PE FA7220

About
FA7220 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Includes Antioxidant. This grade is developed for production of blown film or cast film with good optical properties. When cast on a polished chill roll, the grade produces household cling film with excellent optical and cling properties. CAS-No.: 9002-88-4 Applications FA7220 has been developed especially for applications like: Protective film Laundry and other textile bags Very thin and clear packing films Additives FA7220 contains antioxidant.&&

About

FA7220 is a Low Density Polyethylene for Film Extrusion. Autoclave Technology. Includes Antioxidant. This grade is developed for production of blown film or cast film with good optical properties. When cast on a polished chill roll, the grade produces household cling film with excellent optical and cling properties. CAS-No.: 9002-88-4 Applications FA7220 has been developed especially for applications like: Protective film Laundry and other textile bags Very thin and clear packing films Additives FA7220 contains antioxidant.&&

Product Description
Supplier	Borealis AG
Generic	LDPE
Material Status	Commercial: Active
Features	Optical performance,Inoxidizability,High adhesion degrees,High pressure heat resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.922	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	4.0	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
friction coefficient
With oneself – dynamic	0.80		ISO 8295

film	Nominal value	Unit	Test method
film thickness
test	40	µm
Secant modulus			ASTM D882A
MD：40 µm	200	MPa	ASTM D882A
TD：40 µm	180	MPa	ASTM D882A
tensile strength			ISO 527-3
MD，40 µm	24.0	MPa	ISO 527-3
TD，40 µm	18.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 40 µ m	400	%	ISO 527-3
TD, fracture, 40 µ m	650	%	ISO 527-3
Drop hammer impact
40 µm	80	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD：40 µm	3.0	N	ISO 6383-2
TD：40 µm	2.0	N	ISO 6383-2

THERMAL	Nominal value	Unit	Test method
Melting temperature	111	℃	ISO 11357-3

optical performance	Nominal value	Unit	Test method
gloss
40 µm	110		ASTM D2457
Haze
40 µm	6.0	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	150 to 180	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.