| About |
|---|
| Product Description | |
|---|---|
| Supplier | LANXESS |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Halogen free,Flame Characteristics,Heat Resistance, Good,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 2.1 | % | ISO 62 |
| Saturation, 23 ℃ | 5.5 | % | |
| Shrinkage rate | |||
| TD：150x105x3 mm | 0.006 | cm/cm | ISO 2577 |
| MD：150x105x3 mm | 0.0076 | cm/cm | ISO 2577 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 4200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 60 | MPa | ISO 527-1-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 8.0 | % | ISO 527-1/2 |
| Yield, 23 ℃ | 6.0 | % | ISO 178/A |
| bending strength | |||
| yield | 85 | MPa | ISO 178-A |
| fracture | 100 | MPa | ISO 178-A |
| Bending modulus | 4500 | MPa | ISO 178/A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 55 | kJ/m² | ISO 179/1eU |
| -30℃ | 45 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | <=10.0 | kJ/m² | ISO 180/1A |
| -30℃ | <=10.0 | kJ/m² | ISO 180/1A |
| Impact strength of cantilever beam notch | |||
| 23℃ | <=10.0 | kJ/m² | ISO 180-1A |
| -30℃ | <=10.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | 263 | 10℃/min | ISO 11357-1/-3 |
| Melt Temperature | 290 | ℃ | – |
| Mold temperature | 80 | ℃ | – |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+9 | ohms·cm | IEC 60093 |
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 4.4 | IEC 60250 | |
| 23 ℃，100 Hz | 12.8 | IEC 60250 | |
| Dielectric strength | |||
| 23 ℃，1 mm | 29.0 | kV/mm | IEC 60243-1 |
| Dissipation factor | |||
| 23℃，100Hz | 2.8E-3 | IEC 60250 | |
| 23℃，1MHz | 8.5E-3 | IEC 60250 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |