| Amilan® CM1001R is a Polyamide 6 (Nylon 6) product filled with 40% mineral. It is available in Asia Pacific, Europe, or North America. Characteristics include: Flame Rated Warp Resistant&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low warping |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.90 | % | ISO 62 |
| Molding Shrinkage | |||
| MD:3.0 mm | 0.8-1.0 | % | |
| TD:3.0 mm | 0.8-1.0 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 203 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 173 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 3.00 mm | 21 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 23℃ | 4.5 | 1 kHz | IEC 60250 |
| 23℃ | 3.8 | 1 MHz | IEC 60250 |
| Dissipation factor | |||
| 23℃ | 0.03 | 1 kHz | IEC 60250 |
| 23℃ | 0.02 | 1 MHz | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | HB | UL-94 | |
| 1.50 mm | HB | UL-94 | |
| 3.00 mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | ISO 179/1eU |
| -40℃ | 35 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 81 | M 级 | ISO 2039-2 |
| Rockwell hardness | 119 | R 级 | ISO 2039-2 |
| tensile strength | |||
| 23℃ | 95 | MPa | ISO 527-2 |
| -40℃ | 130 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| -40℃ | 2.0 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 145 | MPa | ISO 178 |
| -40℃ | 160 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 5800 | MPa | ISO 178 |
| -40℃ | 6900 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x80x3mm |
| 3. Without Lubrication |
| 4. 60% RH |
| 5. Tungsten Electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |