| N00M-00 is a fractional melt flow rate, medium term heat aging high impact copolymer polypropylene for blow molding, pipe, tubing and sheet extrusion applications. It offers a superior balance of stiffness and impact strength as compared to competitive impact copolymers of similar melt flow rate. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. This product is not recommended for taste or odor sensitive applications.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,Impact copolymer,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.45 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20 ℃, injection molding | 120 | J/m | ASTM D256 |
| 23 ℃, injection molding | No Break | ASTM D256 | |
| Dart impact equipped with measuring instruments | ASTM D3763 | ||
| -20 ℃, injection molding, toughness failure | No Break | ASTM D3763 | |
| 23 ℃, injection molding, toughness failure | No Break | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, injection molded | 57.8 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, injection molded | 87.8 | ℃ | ASTM D648 |
| Embrittlement temperature | -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 151 | ℃ | ASTM D1525 |
| Relative temperature index | |||
| Electrical performance | 48.9 | ℃ | UL 746 |
| Strength mechanical performance | 48.9 | ℃ | UL 746 |
| Impact mechanical performance | 48.9 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, injection molding | 56 | ASTM D2457 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, injection molding | 23.1 | MPa | ASTM D638 |
| Yield, injection molding | 25.2 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, injection molding | 480 | % | ASTM D638 |
| Yield, injection molding | 9.6 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, injection molding | 1190 | MPa | ASTM D790-A |
| Rockwell hardness | |||
| R-level | 77 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |