| Andur RT 9002 AP is a low viscosity liquid prepolymer which can be processed and cured at room temperature with Curene 107 to yield an elastomer with a hardness of 88 to 92 Shore A. This system has a extended potlife of about 25 minutes that can be adjusted using oleic acid catalyst. Andur RT 9002 AP is recommended where room temperature processing and curing is desired with minimal elastomer shrinkage.&& |
| Product Description | |
|---|---|
| Generic | PUR+TDI |
| Material Status | Commercial: Active |
| Features | Low Viscosity |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 90 | ASTM D2240 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| yield | 14.5 | MPa | ASTM D412 |
| 100% strain | 5.45 | MPa | ASTM D412 |
| 300% strain | 8.27 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D412 |
| Basho’s elasticity | 48 | % | ASTM D2632 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| storage stability | 25 | min |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 690 | cP | ASTM D2393 |
| stripping time | |||
| 22℃ | 6.0 | min |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |