| Geon™ Duracap™ L4605 Red 7640 is a Semi-Rigid Polyvinyl Chloride product. It can be processed by coextrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ Duracap™ L4605 Red 7640 include capstock and outdoor applications.&& |
| Product Description | |
|---|---|
| Generic | PVC, not specified |
| Material Status | Commercial: Active |
| Availabilitys | Latin America,Asia Pacific,Africa & Middle East ,Europe,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, molded | 40 | J/m | ASTM D256 |
| Falling impact resistance | ASTM D4226 | ||
| 23 ℃, extruded blade shape | 70.3 | J/cm | |
| 23℃ | 72.1 | J/cm |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 41.1 | ℃ | |
| 0.45 MPa, annealed, 3.2 mm | 43.9 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 36.1 | ℃ | |
| 1.8 MPa, annealed, 3.18 mm | 36.1 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 7.3E-5 | 1/℃ | ASTM D696 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 5 to 30 | ASTM D523 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 74 | ASTM D2240 | |
| Tensile modulus | 1820 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 23.8 | MPa | ASTM D638 |
| Bending modulus | 1730 | MPa | ASTM D790 |
| bending strength | |||
| yield | 50.7 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Melt Temperature | 182 to 193 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 0.50 in/min |
| 4. Procedure A, C.125 |
| 5. Procedure B, C.125 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |