| About |
|---|
| 20-3236 Resin is a low viscosity copolymer adhesive and potting compound specifically designed for bonding vinyls and neoprenes. 20-3236 Resin has an extended working time and a convenient 2:1 mix ratio. 20-3236 Resin can be used in many difficult bonding applications. It is also used for the encapsulation of vinyl insulated electrical components or sealing vinyl lead wires.&& |
| Product Description | |
|---|---|
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Low Viscosity,Good bond,Copolymer,Agglomerability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Impact strength of cantilever beam notch | 29 | J/m | |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 3000 | cP |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| working temperature | -55.0 to 120 | ℃ | |
| Heating reduction | |||
| After 24 hours at 150℃ | 0.64 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | Amber | ||
| Weight Mix Ratio (PBW) | |||
| Part A | 2.0 | ||
| Part B | 1.0 | ||
| Density | |||
| 25℃ | 1.07 | g/cm³ | |
| Curing time | |||
| 65℃ | 2.0 to 3.0 | hr | |
| 45℃ | 6.0 to 8.0 | hr | |
| 25℃ | 24 to 36 | hr | |
| storage stability | |||
| 25 ℃ | 300 | min | |
| Storage period | 6 | month |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Water absorption rate | 0.21 | % | |
| Shore hardness | |||
| Shaw’s D | 80 | ||
| tensile strength | 57.2 | MPa | |
| Tensile strain | |||
| fracture | 6.4 | % | |
| Relative permittivity | |||
| 1 MHz | 3.57 | ||
| Dissipation factor | |||
| 1 MHz | 0.021 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Catalyzed |
| 3. 100 grams |
| 4. After 24 hours |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |