| ECOZEN BS 100 is eco-friendly bio copolyester which is created using natural materials based on the extract from plant or vegetable materials therefore it does not include environmental hormone bisphenol A (BPA) is a controversial never-ending human hazards. It is useful to sheet extrusion applications because excellent impact strength and high flexural strength and enables to multi-layer sheet with PET, PETG, PC (polycarbonate), ABS, K-resin, Urethane and other resins. It is also suitable for use in the current eco-friendly credit cards because good adhesion of the paper or wood. Key Attributes Excellent Heat Resistance Excellent Impact Strength High Flexural Strength Excellent Chemical & Stain Resistance Excellent 2nd Fabrication High Transparency and Gloss Good Flammability Outstanding Optical Properties BPA / Phthalate free Applications / Uses Outdoor sign boards Disposable food container (for microwave-oven or gas-oven use) Eco-friendly credit cards Deco sheets Sheet/Film for Optical uses&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | 生物基共聚聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,The fouling resistance,High impact resistance,Renewable resources,No BPA,Heat Resistance, Good,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D792 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 89.0 | ℃ | |
| 1.8 MPa, unannealed | 82.0 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 3000 µm | 89.0 | % | ASTM D1003 |
| Haze | |||
| 3000 µm | < 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 111 | ASTM D785 | |
| tensile strength | |||
| TD, yield, 3 mm | 53.0 | MPa | |
| MD, yield, 3 mm | 53.9 | MPa | |
| TD, fracture, 3 mm | 50.0 | MPa | |
| MD, fracture, 3 mm | 53.0 | MPa | |
| Tensile strain | |||
| TD, yield, 3 mm | 5.9 | % | |
| Flow rate, yield, 3 mm | 5.8 | % | |
| TD, fracture, 3 mm | 440 | % | |
| Flow rate, fracture, 3 mm | 480 | % | |
| Bending modulus | |||
| TD，3 mm | 2000 | MPa | |
| MD，3 mm | 2050 | MPa | |
| bending strength | |||
| 3 mm | 84.3 | MPa | |
| 3 mm | 83.4 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.050 in/min |
| 4. Across Flow |
| 5. Flow |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |