| About |
|---|
| 30 % carbon fiber reinforced polyetheretherketone, medium viscosity&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 1.1 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 22800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 217 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/1A/5 |
| Bending modulus | 20500 | MPa | ISO 178 |
| bending strength | 311 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 10 | kJ/m² | ISO 180 |
| Notched impact strength of cantilever beam | 44 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 315 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 0.80 mm | V-0 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| 0.8 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.6 mm | V-0 | IEC 60695-11-10, -20 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 350 to 380 | °C | |
| Mold temperature | 170 to 190 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |