| LONOY lonoy 1300是一种聚碳酸酯+聚丁烯对苯二甲酸酯（PC+PBT）材料,。 该产品在亚太地区或北美洲有供货,加工方式为:注射成型。 LONOY lonoy 1300的主要特性有: 阻燃/额定火焰 美观 耐候性好 典型应用领域包括: 汽车行业 商业/办公用品 工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 40 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：23℃ | 0.80 to 1.0 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.12 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 700 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 450 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.4 mm | 107 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 98.0 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1.6 mm | 28 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| tensile strength | 55.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 90 | % | ASTM D638 |
| Bending modulus | 2200 | MPa | ASTM D790 |
| bending strength | 80.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 85 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Barrel rear temperature | 200 to 220 | °C | |
| Barrel middle temperature | 200 to 225 | °C | |
| Barrel front temperature | 210 to 230 | °C | |
| Processing (melt) temperature | 200 to 230 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | 0.00 to 10.0 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |