Lotte PC-1600 - SOLIAO

About
超低粘度，无着色剂。

Product Description
Supplier	LOTTE
Generic	Polycarbonate
Material Status	Commercial: Active
Features	High purity,Low Viscosity
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt index (300 ℃/1.2kg)	62	g/10 min	ASTM D 1238
Density	1.2	g/cm³	ASTM D792
Shrinkage rate	0.5 – 0.7	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	61	MPa	ASTM D638
Tensile strain
fracture	50	%	ASTM D638
bending strength	90	MPa	ASTM D790
Bending modulus	2352	MPa	ASTM D790

optical performance	Nominal value	Unit	Test method
Transmittance	89	%	ASTM D1003
Haze	<0.8	%	ASTM D1003
Refractive index	1.585		ASTM D542

Process Conditions
injection molding	Nominal value	Unit	Test method
Dry conditions	Nominal value	Unit	Test method
drying temperature	120	°C
Drying time	4	hrs
Maximum moisture content	0.02	%
Melt Temperature	290 – 310	°C
Nozzle temperature	280 – 300	°C
Temperature of the front section of the material barrel	290 – 310	°C
Temperature in the middle section of the barrel	280 – 300	°C
Temperature of the rear section of the barrel	270 – 290	°C
Hopper temperature	60 – 80	°C
Mold temperature	60 – 90	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.