| Amilan® CM1017XL3是一种聚酰胺6（尼龙6）产品,。 它,在亚太地区、北美洲或欧洲有供货。 特性包括: 阻燃/额定火焰 快速成型周期 耐热 良好的韧性&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Low temperature toughness,Heat Stabilized,Quick molding cycle |
| Availabilitys | Europe,North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Shrinkage rate | Internal Method | ||
| MD：1.0 mm | 0.70 to 1.1 | % | Internal Method |
| MD：3.0 mm | 1.2 to 1.8 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr | 1.8 | % | ISO 62 |
| Saturation, 23 ℃ | 11 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40℃ | 3.5 | kJ/m² | ISO 179 |
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -40℃ | 无断裂 | ISO 179 | |
| 23℃ | 无断裂 | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 182 | ℃ | ISO 75-2/B |
| Melting temperature | 225 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 8.0E-5 | 1/℃ | ISO 11359-2 |
| specific heat | 1900 | J/kg/℃ | |
| Thermal conductivity coefficient | 0.25 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 20 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 23 ℃，50 Hz | 4.10 | IEC 60250 | |
| 23 ℃，1 kHz | 3.90 | IEC 60250 | |
| 23 ℃，1 MHz | 3.40 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 23℃，50 Hz | 0.070 | IEC 60250 | |
| 23℃，1 kHz | 0.060 | IEC 60250 | |
| 23℃，1 MHz | 0.030 | IEC 60250 | |
| Arc resistance | 120 | sec | UL 746 |
| Compared to the leakage tracing index | 600 | V | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.79 mm | V-2 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | ||
| R-level | 119 | ISO 2039-2 | |
| R-grade, 80 ℃ | 80 | ISO 2039-2 | |
| tensile strength | ISO 527-2 | ||
| -40℃ | 110 | MPa | ISO 527-2 |
| 23℃ | 80.0 | MPa | ISO 527-2 |
| 80℃ | 25.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Yield, 23 ℃ | 1.5 | % | ISO 527-2 |
| Fracture, 23 ℃ | 38 | % | ISO 527-2 |
| Bending modulus | ISO 178 | ||
| -40℃ | 3800 | MPa | ISO 178 |
| 23℃ | 2800 | MPa | ISO 178 |
| 80℃ | 700 | MPa | ISO 178 |
| bending strength | ISO 178 | ||
| -40℃ | 135 | MPa | ISO 178 |
| 23℃ | 110 | MPa | ISO 178 |
| 80℃ | 40.0 | MPa | ISO 178 |
| compressive strength | |||
| 23℃ | 80.0 | MPa | ISO 604 |
| shear strength | |||
| 23℃ | 70.0 | MPa | ASTM D732 |
| Taber abraser | |||
| 1000 cycles | 3.00 to 4.00 | mg | ISO 9352 |
| friction coefficient | |||
| 0.15 to 0.20 | Suzuki Method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |