| A soft, colorable, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or blow molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Good coloring,Solvent resistance,Ozone resistance,Good Dimensional Stability,Low coefficient of friction,Low or no water absorption,HB,Weather resistance is good,Renewable resources |
| Availabilitys | Latin America,Africa & Middle East ,Asia Pacific,North America,Europe |
| Process Methods | Injection Molding,Multiple injection molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Weathering resistance | f1 | UL 746C | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 5.70 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 5.70 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.20 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 2.20 | MPa | ISO 37 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 470 | % | ISO 37 |
| TD, fracture, 23 ℃ | 470 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 32 | % | ASTM D395B |
| 125℃，70 hr | 60 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 32 | % | ISO 815 |
| 125℃，70 hr | 60 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 64 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -63.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -63.0 | ℃ | ISO 812 |
| Relative temperature index | |||
| Electrical performance | 100 | ℃ | UL 746 |
| Strength mechanical performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 23 ℃，2 mm | 31 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，2.01 mm | 2.30 | IEC 60250 | |
| 23 ℃，2.01 mm | 2.30 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.10 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 177 to 191 | °C | |
| Barrel middle temperature | 179 to 193 | °C | |
| Barrel front temperature | 185 to 199 | °C | |
| Nozzle temperature | 185 to 210 | °C | |
| Processing (melt) temperature | 143 to 216 | °C | |
| Mold temperature | 24 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Melt temperature | 179 to 216 | °C | |
| Nozzle temperature | 177 to 216 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1 |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |