| About |
|---|
| CALIBRE™ IM 401-11 Impact Modified Polycarbonate resin is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy processing with improved impact strength in highly filled formulations. Main Characteristics: Impact modified Superior low temperature toughness Applications: Automotive interiors Automotive exteriors Small & large applications&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,High impact resistance,low-temperature impact resistance,HB |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ASTM D792 |
| Density | 1.18 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 11 | g/10min | ASTM D1238 |
| 300℃，1.20kg | 11 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.60 to 0.80 | % | ISO 294-4 |
| MD | 0.60 to 0.80 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 56.0 | MPa | ISO 527-2/50 |
| yield | 55.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 130 | % | ISO 527-2/50 |
| fracture | 130 | % | ASTM D638 |
| Bending modulus | 2280 | MPa | ASTM D790 |
| Bending modulus | 2270 | MPa | ISO 178 |
| bending strength | 89.6 | MPa | ASTM D790 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 690 | J/m | ASTM D256 |
| 23℃ | 690 | J/m | ISO 180-4A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 56.5 | J | ASTM D3763 |
| Tensile impact strength | 630 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 136 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 136 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 121 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 121 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 146 | ℃ | ASTM D1525 7 |
| B50 | 146 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Method I (3 point load), 0.079 in/min |
| 4. 0.079 in/min |
| 5. 3-points |
| 6. 11.1 ft/sec |
| 7. Rate A (50°C/h), Loading 2 (50 N) |
| 8. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |