| CALIBRE™ 300-10 聚碳酸酯树脂具有优异的抗冲击性能、耐热畸变性能和光学透明度。CALIBRE 300-10 系列产品包含有4种添加剂产品类型： CALIBRE 300：无脱模剂或者抗紫外线稳定剂。CALIBRE 301：含脱模剂。 CALIBRE 302：含抗紫外线稳定剂。CALIBRE 303：含脱模剂和抗紫外线稳定剂。 政府和业界标准： 加拿大标准协会(CSA)的要求 美国安全检测实验室 (UL)的要求 应用领域： 电器产品 存储介质外层 商用设备 电子元器件 照明装置 运输设备 家用器具 娱乐产品 包装应用&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,HB,V-2 |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ISO 62 |
| 23℃，24hr | 0.15 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 13 | kJ/m² | ISO 179/1eA |
| 23℃ | 35 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 90 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 141 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 125 | ℃ | ISO 75-2/A |
| 0.45 MPa, annealed | 144 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 149 | ℃ | ISO 306 |
| Ball pressure temperature | > 125 | ℃ | IEC 60335-1 |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric constant | IEC 60250 | ||
| 60 Hz | 3.00 | IEC 60250 | |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| 2.00 mm, solution A | 250 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 3.00 mm | HB | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.0 mm | 900 | ℃ | IEC 60695-2-12 |
| 2.0 mm | 875 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 875 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1 mm | 800 | ℃ | IEC 60695-2-13 |
| 2 mm | 775 | ℃ | IEC 60695-2-13 |
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 26 | % | ISO 4589-2 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ISO 527-2/50 |
| tensile strength | |||
| fracture | 71.0 | MPa | ISO 527-2/50 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 150 | % | ISO 527-2/50 |
| yield | 6.0 | % | ISO 527-2/50 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 97.0 | MPa | ISO 178 |
| Taber abraser | 45 | % | ISO 9352 |
| Rockwell hardness | ISO 2039-2 | ||
| M-level | 73 | ISO 2039-2 | |
| R-level | 118 | ISO 2039-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |