| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High liquidity,Good stripping performance,Heat Stabilized,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.80 to 1.0 | % | ISO 294-4 |
| MD | 0.20 to 0.40 | % | ISO 294-4 |
| Relative viscosity | 2.9 | ISO 307 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10200 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 175 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2 |
| Bending modulus | 8800 | MPa | ISO 178 |
| bending strength | 280 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 85 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 244 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 250 | ℃ | ISO 306 |
| melting point | 261 | ℃ | ISO 11357 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 | °C | |
| Drying time – hot air dryer | 2.0 to 12 | hr | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |