| PRE-ELEC® CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® CP 1319 has excellent mechanical properties and is easy to extrude. Typical applications include blown mono- or co-extrusion film for ESD bags and innerliners, bags or layflat tubing for hazardous powders. PRE-ELEC® CP 1319 is also suitable for extrusion foam applications.&& |
| Product Description | |
|---|---|
| Supplier | Premix Oy |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Conductive |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ASTM D792 |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，10.0kg | 4.5 | g/10min | ISO 1133 |
| 190℃，5.0kg | 1.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| TD | 15.2 | MPa | ASTM D638 |
| MD | 19.3 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| TD, yield | 13.1 | MPa | ASTM D638 |
| MD, yield | 13.1 | MPa | ASTM D638 |
| tensile strength | ISO 527-2 | ||
| TD, yield | 13.0 | MPa | ISO 527-2 |
| MD, yield | 13.0 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| — | 15.0 | MPa | ISO 527-2 |
| — | 19.0 | MPa | ISO 527-2 |
| Tensile strain | ASTM D638 | ||
| TD, yield | 60 | % | ASTM D638 |
| Flow rate, yield | 70 | % | ASTM D638 |
| Tensile strain | ISO 527-2 | ||
| TD, yield | 60 | % | ISO 527-2 |
| Flow rate, yield | 70 | % | ISO 527-2 |
| Tensile strain | ASTM D638 | ||
| fracture | > 600 | % | ASTM D638 |
| Flow rate, fracture | > 600 | % | ASTM D638 |
| Tensile strain | ISO 527-2 | ||
| fracture | > 600 | % | ISO 527-2 |
| fracture | > 600 | % | ISO 527-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+4 | ohms | ESD STM11.11 |
| Surface resistivity | < 1.0E+4 | ohms | IEC 61340-2-3 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 60 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 180 | °C | |
| Barrel 2 zone temperature | 180 | °C | |
| Barrel 3 zone temperature | 190 | °C | |
| Barrel 4 zone temperature | 190 | °C | |
| Barrel 5 zone temperature | 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Across Flow |
| 3. Flow |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |