XYLEX™ EXXX0292 Resin

About
XYLEX™ EXXX0292是一个透明的共聚酯/聚碳酸酯与混合树脂，高流动性， V2 UL94 （ 1.5mm，玻璃化转变温度108°C）

Product Description
Supplier	SABIC
Generic	PC+PET
Material Status	Commercial: Active
Features	Good Clarity,High liquidity
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 50 mm/min	60	MPa	ISO 527
Fracture, 50 mm/min	50	MPa	ISO 527
Tensile strain
Yield, 50 mm/min	5	%	ISO 527
Fracture, 50 mm/min	125	%	ISO 527
Tensile modulus
1 mm/min	2100	MPa	ISO 527
bending strength
Yield, 2 mm/min	84	MPa	ISO 178
Bending modulus
2 mm/mim	2000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	10	kJ/m²	ISO 179/2C
-30℃	5	kJ/m²	ISO 179/2C
Charpy Unnotch Impact strength
23℃	NB	kJ/m²	ISO 179/2C
-30℃	NB	kJ/m²	ISO 179/2C
Impact strength of cantilever beam notch
23℃	120	J/m	ASTM D256
0℃	90	J/m	ASTM D256
-30℃	20	J/m	ASTM D256
Notched impact strength of cantilever beam
23℃	NB	kJ/m²	ISO 180/1U
-30℃	NB	kJ/m²	ISO 180/1U
Impact strength of cantilever beam notch
23℃，80104	7	kJ/m²	ISO 180-1A
0℃，80104	6	kJ/m²	ISO 180-1A
80104 -30℃	3	kJ/m²	ISO 180-1A
Notched impact strength of cantilever beam
23℃，80104	NB	kJ/m²	ISO 180/1U
-30℃，80104	NB	kJ/m²	ISO 180/1U

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp
A50	115	℃	ASTM D1525
B50	108	℃	ASTM D1525
Hot deformation temperature
0.45 MPa, 100 mm span	100	℃	ISO 75/Bf
1.8 MPa, 100 mm span	90	℃	ISO 75/Af
Unannealed, 3.2 mm
Linear expansion coefficient, -40 ℃ to 40 ℃
flow	5.6E-05	1/℃	ISO 11359-2
0.45MPa	100	℃	ASTM D 648
transverse	6.4.E-05	1/℃	ISO 11359-2
1.8MPa	90	℃	ASTM D 648
Vicat Softening Temp
A50	115	℃	ISO 306
B50	108	℃	ISO 306
B120	110	℃	ISO 306

PHYSICAL	Nominal value	Unit	Test method
Density	1.22		ASTM D792
Shrinkage rate
MD：3.2 mm	0.4 – 0.6	%	Internal Method
Shrinkage rate
MD：3.2 mm	0.4 – 0.6	%	Internal Method
Melt Flow Rate
265℃，2.16kg	21	g/10min	ASTM D1238
300℃，1.20kg	37	g/10min	ASTM D1238
Density	1.22	g/cm³	ISO 1183
Apparent viscosity of melt
300℃，1500 sec-1	90	Pa-s	ISO 11443
Melt Volume Rate
265℃，2.16 kg	18	cm³/10min	ISO 1133
300℃，1.2 kg	33	cm³/10min	ISO 1133

optical performance	Nominal value	Unit	Test method
Transmittance
2.54 mm	0.9	%	ASTM D1003
Haze
2.54 mm	89	%	ASTM D1003

Process Conditions
injection molding	Nominal value	Unit	Test method
Drying temperature	65 – 80	°C
Drying time	3 – 5	hrs
Drying time (cumulative)	8	hrs
Maximum water content	0.02	%
Melt temperature	250 – 290	°C
Nozzle temperature	250- 290	°C
Front Section Zone 3 Temperature	250 – 290	°C
Temperature in Zone 2 of the middle section	245 – 280	°C
Temperature in Zone 1 of the rear section	245 – 255	°C
Mold temperature	40 – 60	°C
Back pressure	0.2 – 0.5	MPa
Screw speed	20 – 100	rpm
Shoot to cylinder size	40 – 80	%
Depth of exhaust groove	0.013 – 0.02	mm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.