| About |
|---|
| Advanced-PP 1128 N is a propylene homopolymer & suited for cast film application. It contains slip & antiblocking agents. Application Cast film & water quenchied tubular film Regulatory Information: The Grade Advanced-PP 1128N and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011 (and its amendments). Specific information is available upon request.&& |
| Product Description | |
|---|---|
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking,Homopolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile strain | DIN 53455 | ||
| MD, fracture, 50 µ m, cast thin film | 680 | % | DIN 53455 |
| TD, fracture, 50 µ m, cast thin film | 720 | % | DIN 53455 |
| Drop hammer impact | |||
| 50 µ m, cast thin film | 280 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| A50 | 154 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 163 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20 °, 50 µ m, cast thin film | 100 | ISO 2813 | |
| Haze | |||
| 1000 µ m, injection molding | 2.7 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | DIN 53455 | ||
| MD，50 µm | 42.0 | MPa | DIN 53455 |
| TD，50 µm | 38.0 | MPa | DIN 53455 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 76.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1500 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 35.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 9.0 | % | ISO 527-2/50 |
| fracture | > 50 | % | ISO 527-2/50 |
| Bending modulus | DIN 53121 | ||
| MD, 0.05 mm, cast thin film | 700 | MPa | DIN 53121 |
| TD, 0.05 mm, cast thin film | 670 | MPa | DIN 53121 |
| friction coefficient | 0.18 | DIN 53375 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Cast Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |