| Starflam RF0055E is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, Polyamide 66 / Polyamide 6 Injection Molding Resin (also known as RF1005Z250EM)&& |
| Product Description | |
|---|---|
| Supplier | Ascend |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | V-1,V-0 |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.10 to 0.30 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 140 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| Bending modulus | 8400 | MPa | ISO 178 |
| bending strength | 190 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 40 | kJ/m² | ISO 180/1U |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 64 mm span | 210 | ℃ | ISO 75-2/Af |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-1 | UL 94 | |
| 1.20 mm | V-0 | UL 94 | |
| 1.60 mm, E2P measurement | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.20 | % | |
| Barrel rear temperature | 265 to 275 | °C | |
| Barrel middle temperature | 265 to 275 | °C | |
| Barrel front temperature | 270 to 280 | °C | |
| Processing (melt) temperature | 270 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 80x10x4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |