| Glastic SG-200 high-strength and high-temperature laminate offers the same high-performance features and benefits as Glastic’s FHT Laminate. In addition, SG-200 offers much higher mechanical strengths than FHT with temperature ratings of up to 210°C. Glastic SG-200 is also a superior replacement material for epoxy-bonded mica in layer insulation applications.&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High Heat Resistance,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24hr | 0.30 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1.60 mm | 11700 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 1.60 mm | 86.2 | MPa | ASTM D638 |
| bending strength | |||
| Yield, 1.60 mm | 200 | MPa | ASTM D790 |
| compressive strength | |||
| 1.60 mm | 248 | MPa | ASTM D695 |
| shear strength | 76.5 | MPa | ASTM D732 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 1.6mm | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| MD：1.6 mm | 2.0E-5 | 1/℃ | ASTM D696 |
| Thermal conductivity coefficient | 0.25 | W/m/K | ASTM C177 |
| Relative temperature index | |||
| Electrical performance, 1.60 mm | 210 | ℃ | UL 746 |
| 1.60 mm | 210 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.5E+10 | ohms | ASTM D257 |
| Dielectric strength | ASTM D149 | ||
| 1.6 mm in air | 20 | kV/mm | ASTM D149 |
| 1.6 mm in oil | 25 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 1.60 mm，60 Hz | 4.60 | ASTM D150 | |
| 1.60 mm，1 MHz | 3.70 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1.60 mm，60 Hz | 0.037 | ASTM D150 | |
| 1.60 mm，1 MHz | 0.013 | ASTM D150 | |
| Arc resistance | |||
| 1.60 mm | 120 | sec | ASTM D495 |
| Compared to the resistance to leakage and marking index | |||
| 1.60 mm | 500 | V | UL 746 |
| High Arc Burning Index (HAI) (1.60 mm) | 200 | UL 746 | |
| High voltage arc marking rate (HVTR) (1.60 mm) | 0.00 | mm/min | UL 746 |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 0.711 mm | 35 | sec | UL 746 |
| 1.47 mm | 39 | sec | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Extreme oxygen index | |||
| 1.6 mm | 22 | % | ASTM D2863 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |