Ultramid® B3WG10 BK00564

About
This resin is a heat stabilized, 50% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black weather resistant and pigmented versions. Applications Ultramid B3WG10 BK00564 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.&&

About

This resin is a heat stabilized, 50% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black weather resistant and pigmented versions. Applications Ultramid B3WG10 BK00564 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.&&

Product Description
Supplier	BASF
Generic	PA6
Material Status	Commercial: Active
Features	Good Rigidity,Good Dimensional Stability,Grease resistance,Heat Stabilized
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.56	g/cm³	ISO 1183
Water absorption rate			ISO 62
Saturation, 23 ℃	4.8	%	ISO 62
Equilibrium, 23 ℃, 50% RH	1.4	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	16700	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	225	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	2.5	%	ISO 527-2
Bending modulus
23℃	14500	MPa	ISO 178
bending strength
23℃	345	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	15	kJ/m²	ISO 179
Charpy Unnotch Impact strength
23℃	90	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
-40℃	12	kJ/m²	ISO 180
23℃	15	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	220	℃	ISO 75-2/B
1.8 MPa, unannealed	215	℃	ISO 75-2/A
Melting temperature
DSC	220	℃	ISO 3146

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.060	%
Processing (melt) temperature	280 to 305	°C
Mold temperature	80 to 95	°C
Injection pressure	3.45 to 10.3	MPa
Injection speed	快速

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.