MERICAN® 30-200P

About
EPOXY VINYL ESTER RESIN (VARIM) MERICAN® 30-200P is a low-viscosity, prepromoted, high performance epoxy vinyl ester resin. It owns excellent properties both in mechanical and processing, fatigue resistance. MERICAN 30-200P is suitable for Vacuum Infusion Process. PROPERTY Low-viscosity Shorter geltime drift, good storage stability Low peak exotherm, thick pieces can be formed at one time Good curing properties, thoroughly curing for thin pieces Excellent mechanical properties, good adhesion between laminates Resistant to fatigue, aging and corrosion APPLICATION Suitable for the fabricatiion of composites products with high performance and complex structure, especially large windmill blades and yachts, etc. Suitable for vacuum infusion process&&

About

EPOXY VINYL ESTER RESIN (VARIM) MERICAN® 30-200P is a low-viscosity, prepromoted, high performance epoxy vinyl ester resin. It owns excellent properties both in mechanical and processing, fatigue resistance. MERICAN 30-200P is suitable for Vacuum Infusion Process. PROPERTY Low-viscosity Shorter geltime drift, good storage stability Low peak exotherm, thick pieces can be formed at one time Good curing properties, thoroughly curing for thin pieces Excellent mechanical properties, good adhesion between laminates Resistant to fatigue, aging and corrosion APPLICATION Suitable for the fabricatiion of composites products with high performance and complex structure, especially large windmill blades and yachts, etc. Suitable for vacuum infusion process&&

Product Description
Supplier	Huachang
Generic	乙烯基酯
Material Status	Commercial: Active
Features	Low Exotherm,Low Viscosity,Corrosion Resistant,Good bond,Fatigue resistance
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Solid content	52 to 56	%

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	110	℃	ASTM D648
thermal stability
80℃	> 2	day

Thermosetting mixed viscosity	Nominal value	Unit
25℃	100 to 200	cP
Gelation time
25℃	> 2.0	hr

Supplementary information	Nominal value	Unit	Test method
exothermic peak
25℃	80 to 130	℃

MECHANICAL	Nominal value	Unit	Test method
Babbitt hardness	40		ASTM D2583
Tensile modulus	3400	MPa	ASTM D638
tensile strength	90.0	MPa	ASTM D638
Tensile strain
fracture	5.0	%	ASTM D638
Bending modulus	3400	MPa	ASTM D790
bending strength	140	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
2. 100 gm
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.