| Maleated PE Coupling Agent LINXIDAN® LX4433 is a Maleated PE Coupling Agent designed specifically to chemically bind natural fibers to PE in Wood-Plastic Composites. Coupling fibers to the PE matrix, in a 50% wood-filled system, reduces moisture uptake while increasing flexural modulus by 20% and overall flexural strength by 90%.&& |
| Product Description | |
|---|---|
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Low moisture absorption |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.60 | g/10min | ASTM D1238 |
| Maleic anhydride content | High | Internal Method | |
| Water absorption rate | |||
| submersion | 8.3 | day | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | |||
| — | 2920 | MPa | |
| — | 3390 | MPa | |
| — | 3520 | MPa | |
| bending strength | |||
| — | 35.0 | MPa | |
| — | 59.4 | MPa | |
| — | 66.8 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| — | 64 | J/m | |
| — | 210 | J/m | |
| — | 220 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 130 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Referenced Maleic Anhydride levels should be considered as: Low: <0.25 Wt% / Medium: 0.25-0.75 Wt% / High: 0.75-1.25 Wt% / Very High: >1.25 Wt%. |
| 3. 2% in LINXIDAN® LX4433 in 50% Wood Filled PE |
| 4. 1% in LINXIDAN® LX4433 in 50% Wood Filled PE |
| 5. 0% in LINXIDAN® LX4433 in 50% Wood Filled PE |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |