| About |
|---|
| Description HU300 is a new class of high crystallinity homo polypropylene with extremely high stiffness and excellent heat resistance. HU300 is designed for the production of BOPP films Characteristics Superior mechanical properties; HU300 is suitable for replacement of PET Excellent thermal stability ; Stable thermal shrinkage at high temperature High melting temperature of BOPP Film : 173°C&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP homopolymerization |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Food contact compliance,High Heat Resistance,High crystallization,Heat Stabilized,Homopolymer |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | ASTM D882 | ||
| MD | 2260 | MPa | ASTM D882 |
| TD | 3430 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| yield | 41.2 | MPa | ASTM D638 |
| MD, fracture | 147 | MPa | ASTM D882 |
| TD, fracture | 275 | MPa | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 29 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 117 | ℃ | ASTM D648 |
| Melting temperature | 173 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 | |
| Tensile strain | |||
| fracture | 400 | % | ASTM D638 |
| Bending modulus | 1960 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |