| EcoPaXX®是我司生物基材的高性能尼龙（PA410)，各方面性能卓越，原材料主要来自热带蓖麻籽，不参与食物链竞争。&&EcoPaXX®属于长链聚酰胺，即使在最严苛的使用情况下，表现依旧无与伦比，其中包括绝佳的耐化学性，极低的吸水性，超高的熔点（生物基塑料中堪称第一）以及快速的结晶速率（与PA66、PA46相仿）&&此外，EcoPaXX®已被验证整个生命周期100%碳中立。这代表在生产EcoPaXX过程中所产生的二氧化碳量可被植物生长过程中吸收的二氧化碳量所抵消，因为热带蓖麻籽的含量在EcoPaXX中高达70%。 |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 410 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good stripping performance,Solvent resistance |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt volume flow velocity | 11 / * | cm³/10min | ISO 1133 |
| temperature | 290 / * | °C | ISO 1133 |
| load | 5 / * | kg | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.6 / * | % | ISO 294-4 |
| Shrinkage rate | |||
| MD | 1.2 / * | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11000 / 8200 | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 120℃ | 5000 / – | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 160℃ | 4000 / * | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 180℃ | 3200 / * | MPa | ISO 527-1-2 |
| Tensile modulus | |||
| 200℃ | 2700 / * | MPa | ISO 527-1-2 |
| Fracture stress | 180 / 130 | MPa | ISO 527-1/-2 |
| Fracture stress (120 ° C) | 90 / – | MPa | ISO 527-1/-2 |
| Fracture stress (160 ° C) | 70 / * | MPa | ISO 527-1/-2 |
| Tensile stress (180 ° C) | 60 / * | MPa | ISO 527-1/-2 |
| Tensile stress (200 ° C) | 50 / * | MPa | ISO 527-1/-2 |
| Tensile strain | |||
| fracture | 4 / 5.4 | % | ISO 527-1/2 |
| Fracture strain (120 ° C) | 9.5 / – | % | ISO 527-1/-2 |
| Fracture strain (160 ° C) | 10.5 / * | % | ISO 527-1/-2 |
| Fracture strain (180 ° C) | 11 / * | % | ISO 527-1/-2 |
| Fracture strain (200 ° C) | 12 / * | % | ISO 527-1/-2 |
| Bending modulus | 10500 / 8100 | MPa | ISO 178 |
| bending strength | 270 / 190 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 250 / * | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 1.8 MPa | 220 / * | ℃ | ISO 75-1/2 |
| Hot deformation temperature | |||
| 0.45 MPa | 243 / * | ℃ | ISO 75-1/2 |
| Linear coefficient of thermal expansion | |||
| TD | 0.4E-4 | /℃ | ISO 11359-1/-2 |
| Linear coefficient of thermal expansion | |||
| MD | 0.6E-4 | /℃ | ISO 11359-1/-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1E15 | ohms·cm | IEC 60093 |
| Dielectric strength | 38 / 37 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | – / 600 | V | IEC 60112 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Moisture absorption rate | 1.2 / * | % | Sim. to ISO 62 |
| Biomass content | 67 / * | % (Bio C/Total C) | ASTM D6866-12 Method B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 90 / 90 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| -30℃ | 14 / – | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength | |||
| 23℃ | 20 / 25 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |