| About |
|---|
| Lowest molecular weight, suitable crystallinity, good compatibility with ABS, best rheological property, suitable for production of molded products, Used as a flame retardant and compatibilier in ABS.&& |
| Product Description | |
|---|---|
| Supplier | Pujie |
| Generic | CPE |
| Material Status | Commercial: Active |
| Features | Low molecular weight |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Apparent density | > 0.50 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 40 | g/10min | |
| Chlorine content | 35.0 | wt% | |
| Sieve Residue（40 Mesh） | > 98 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Fusion heat | 16.0 to 24.0 | J/g |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Impurities | < 25.0 | pcs/50 g | |
| Whiteness（E457） | > 90.0 | ° | |
| volatility | < 0.40 | % | |
| decomposition temperature | > 175 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | < 75 | ||
| tensile strength | > 6.00 | MPa | |
| Tensile strain | |||
| fracture | > 700 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |