| About |
|---|
| Provisional – PP Homopolymer for tubular water quenched film PP 5201L is specially developed for tubular water quenched blown film applications with suitable dosage of slip and antiblock additives. Films produced using PP 5201L have the following features: Good processability Good optical properties High melt Strength Excellent runability on bagging and sealing machines Typical Applications PP 5201L can be used for producing packaging for garments, textiles, stationery and food.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Smoothness,Optical performance,High anti-blocking,Homopolymer |
| Availabilitys | North America,Latin America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 11 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 23 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ASTM D648 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| tensile strength | |||
| Yield, injection molding | 35.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Yield, injection molding | 10 | % | ASTM D638 |
| Bending modulus | |||
| 1% cut, injection molding | 1450 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 205 to 215 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. Rate B (120°C/h) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |