Marlex® TRB-115

About
This bimodal high molecular weight, high density polyethylene (HMW-HDPE) ethylene-hexene copolymer is tailored for blown film applications that require: Good bubble stability and film drawdown High impact strength and toughness Excellent stiffness and tensile strength Balanced tear strength Typical blown film applications include: T-shirt bags Produce bags Merchandise bags Industrial liners Trash can liners This resin meets these specifications: FDA 21 CFR 177.1520(c) 3.2a. The resin may be used in contact with all types of food as defined in Table 1, 21 CFR 176.170(c) and at use conditions B-H as defined in Table 2, 21 CFR 176.170(c).

About

This bimodal high molecular weight, high density polyethylene (HMW-HDPE) ethylene-hexene copolymer is tailored for blown film applications that require: Good bubble stability and film drawdown High impact strength and toughness Excellent stiffness and tensile strength Balanced tear strength Typical blown film applications include: T-shirt bags Produce bags Merchandise bags Industrial liners Trash can liners This resin meets these specifications: FDA 21 CFR 177.1520(c) 3.2a. The resin may be used in contact with all types of food as defined in Table 1, 21 CFR 176.170(c) and at use conditions B-H as defined in Table 2, 21 CFR 176.170(c).

Product Description
Supplier	Chevron Phillips
Generic	HDPE
Material Status	Commercial: Active
Features	Good flexibility,High impact resistance,Good dissection,High molecular weight,Good tear strength,High density,Bimodal molecular weight distribution,Hexene copolymers
Availabilitys	North America,Latin America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.950	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	0.060	g/10min
190℃，21.6kg	9.5	g/10min

film	Nominal value	Unit	Test method
film thickness	13	µm
Secant modulus
1% secant, MD: 13 µ m, blow molded film	827	MPa
1% secant, TD: 13 µ m, blow molded film	965	MPa
Tensile strength
MD: fracture, 13 µ m, blow molded film	90.0	MPa
TD: fracture, 13 µ m, blow molded film	41.0	MPa
Tensile strain
MD, fracture, 13 µ m, blow molded film	260	%
TD, fracture, 13 µ m, blow molded film	570	%
Drop hammer impact
13 µ m, blow molded film	260	g	ASTM D1709
Elmandorf tear strength
MD: 13 µ m, blow molded film	15	g
TD: 13 µ m, blow molded film	450	g

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.