| EMERGE™ PC 8600 is a translucent ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications. Applications: Information Technology Equipment Power adaptors&& |
| Product Description | |
|---|---|
| Supplier | Trinseo |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 750 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, 3.20 mm, injection molding, total energy | 58.8 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 139 | ℃ | |
| 1.8 MPa, unannealed | 127 | ℃ | |
| Vicat Softening Temp | 149 | ℃ | ASTM D1525 2 |
| Linear coefficient of thermal expansion | |||
| MD：-40~82℃ | 6.5E-5 | 1/℃ | ASTM D696 |
| Relative temperature index | |||
| Electrical performance, 3.20 mm | 125 | ℃ | UL 746 |
| Impact mechanical performance, 3.20 mm | 125 | ℃ | UL 746 |
| 3.20 mm | 125 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glowing wire flammability index | |||
| 1.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Extreme oxygen index | 35 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 3.20 mm | 123 | ASTM D785 | |
| Tensile modulus | |||
| 3.20 mm, injection molded | 2210 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 60.0 | MPa | |
| Fracture, 3.20 mm, injection molded | 57.9 | MPa | |
| Tensile strain | ASTM D638 | ||
| Yield, 3.20 mm, injection molding | 6.2 | % | |
| Fracture, 3.20 mm, injection molded | 110 | % | |
| Bending modulus | |||
| 3.20 mm, injection molded | 2400 | MPa | ASTM D790 |
| bending strength | |||
| 3.20 mm, injection molded | 93.8 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 271 to 288 | °C | |
| Mold temperature | 65.6 to 98.9 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 11.1 ft/sec |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |