| Descriptions: DESLON™ DSC104GM is one of the brands which made by Polyamide6 that filled Glass Fiber & Mineral Filler 40%. It provides good mechanical property and good heat resistance property. Applications: DESLON™ DSC104GM is one of the most-used for surface appearance, good mechanical property and heat resistance goods due to excellent fluidity, such as Roof Rack, etc.&& |
| Product Description | |
|---|---|
| Supplier | DESCO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Good liquidity,High Heat Resistance,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.30 to 0.50 | % | |
| Water absorption rate | |||
| 23℃，24hr | 1.0 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 49 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 140 | ℃ | ASTM D648 |
| Melting temperature | 220 | ℃ | DSC |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| tensile strength | 98.1 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 7850 | MPa | ASTM D790 |
| bending strength | 167 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 120 | °C | |
| Drying time | 3.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.20 | % | |
| Barrel rear temperature | 240 to 250 | °C | |
| Barrel middle temperature | 250 to 260 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 255 to 270 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 80 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |