RTV-2 P-15B - SOLIAO

About
P-10, P-15 and P-20 RTV silicone rubbers are two-component, platinum-catalyzed systems that cure at room temperature. All of these materials have low viscosity, high elongation, high tear strength and low durometer. They are easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show inhibition sensitivity. P-10, P-15 and P-20 offer excellent release properties and are extremely useful for casting complex shapes, animatronic skins, or any application where exceptional flexibility and tear resistance are required.&&

About

P-10, P-15 and P-20 RTV silicone rubbers are two-component, platinum-catalyzed systems that cure at room temperature. All of these materials have low viscosity, high elongation, high tear strength and low durometer. They are easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component silicone rubbers exhibit excellent chemical and heat resistance, but may show inhibition sensitivity. P-10, P-15 and P-20 offer excellent release properties and are extremely useful for casting complex shapes, animatronic skins, or any application where exceptional flexibility and tear resistance are required.&&

Product Description
Generic	硅橡胶,RTV-2
Material Status	Commercial: Active
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.08	g/cm³

Thermosetting mixed viscosity	Nominal value	Unit	Test method

Uncured Properties	Nominal value	Unit
colour	Translucent
viscosity	25 to 35	Pa·s
Curing time	16 to 18	hr
storage stability	60 to 120	min

Cured Properties	Nominal value	Unit	Test method
Shore hardness
Shaw’s A	11 to 19
Shaw’s A	14 to 22
tensile strength	2.93 to 3.62	MPa	ASTM D412
Tensile strain
fracture	410 to 510	%	ASTM D412
tear strength	13.1 to 21.9	kN/m	ASTM D624
Coverage（Cured）	0.925	cm³/g

THERMAL	Nominal value	Unit
Operating temperature
Cured	-51 to 288	℃
Thermosetting components
resin	按容量计算的混合比: 100 按重量计算的混合比: 10
Hardening method	按容量计算的混合比: 11 按重量计算的混合比: 1.0
Storage period	26	wk

Notes
1. Typical properties: these are not to be construed as specifications.
2. Mixed
3. Base
4. 1 Day
5. 7 Days
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.