ALCUDIA® EBA PA-303

About
EBA ALCUDIA® PA-303 is a copolymer suitable for blown film applications with good optical and mechanical properties even at low temperatures. The material has very good sealing properties. The butyl acrylate content is 3%. TYPICAL APPLICATIONS Shrink film Silage film Heavy-duty bags Recommended melt temperature 180°C. Processing characteristics of PA-303 are similar to LDPE and conventional polyethylene extruders are recommended.&&

About

EBA ALCUDIA® PA-303 is a copolymer suitable for blown film applications with good optical and mechanical properties even at low temperatures. The material has very good sealing properties. The butyl acrylate content is 3%. TYPICAL APPLICATIONS Shrink film Silage film Heavy-duty bags Recommended melt temperature 180°C. Processing characteristics of PA-303 are similar to LDPE and conventional polyethylene extruders are recommended.&&

Product Description
Supplier	REPSOL
Generic	EBA
Material Status	Commercial: Active
Features	Good heat sealing,Optical performance,Food contact compliance
Availabilitys	North America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.923	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.30	g/10min	ISO 1133
Butyl acrylate composition	3.0	wt%

film	Nominal value	Unit	Test method
film thickness
test	130	µm
tensile strength			ISO 527-3
MD, fracture, 130 µ m, blow molded film	25.0	MPa	ISO 527-3
TD, fracture, 130 µ m, blow molded film	25.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 130 µ m, blow molded film	500	%	ISO 527-3
TD, fracture, 130 µ m, blow molded film	700	%	ISO 527-3
Drop hammer impact
130 µ m, blow molded film	600	g	ISO 7765-1
Elmandorf tear strength			ISO 6383-2
MD: 130 µ m, blow molded film	4.0	N	ISO 6383-2
TD: 130 µ m, blow molded film	6.0	N	ISO 6383-2

optical performance	Nominal value	Unit	Test method
gloss
45 °, 125 µ m, blow molded film	70		ASTM D2457
Haze
125 µ m, blow molded film	10	%	ASTM D1003

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	180	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.