| SABIC® HDPE F04660 is a high density polyethylene blow moulding grade for high rigidity, good toughness and processability. These properties offer bottles to be made at lower weight with good top load strength. Typical applications. SABIC® HDPE F04660 can be used in hollow thinwalled parts and profile extrusions. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,High density |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.70 | g/10min | |
| 190℃，21.6kg | 46 | g/10min | |
| 190℃，5.0kg | 3.0 | g/10min | |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, molded, F50 | 15.0 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, molded | 6.0 | kJ/m² | |
| 23 ℃, molded | 10 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 88.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 129 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 134 | ℃ | ISO 11357-3 |
| Enthalpy Change | 223 | J/g | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow molding barrel temperature | 175 to 200 | ℃ | |
| Blow Molding Melt Temperature | 205 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 63 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1250 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 29.0 | MPa | |
| Fracture, 2 mm, molded | 18.0 | MPa | |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| Bending modulus | |||
| 2 mm, molded into shape | 1550 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 31.0 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |