| About |
|---|
| ASA Compound, UV stabilized&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | ASA |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good liquidity,HB |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 220℃，10 kg | 17.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 72 | kJ/m² | ISO 179/1eU |
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 92.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 80.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 105 | ℃ | ISO 306/A50 |
| B50 | 97.0 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | |||
| Solution A | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.6 mm | HB | IEC 60695-11-10, -20 | |
| 3.2 mm | HB | IEC 60695-11-10, -20 | |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 700 | ℃ | IEC 60695-2-13 |
| 3 mm | 700 | ℃ | IEC 60695-2-13 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 85.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2200 | MPa | ISO 527-2/1A/1 |
| tensile strength | ISO 527-2/1A/50 | ||
| yield | 47.0 | MPa | ISO 527-2/1A/50 |
| fracture | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 3.6 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 10 | % | ISO 527-2/1A/50 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | |||
| 4.50% strain | 72.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Proposed maximum recycled material ratio | 30 | % | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 40 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |