Celstran® PA66-GF50-01

About
Material code according to ISO 1043-1: PA66 Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

About

Material code according to ISO 1043-1: PA66 Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.&&

Product Description
Supplier	Celanese
Generic	PA66
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,Good flexibility,Corrosion Resistant,low-temperature impact resistance,Good Isotropy
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	16500	MPa
tensile strength
fracture	255	MPa
Tensile strain
fracture	2.1	%
Bending modulus
23℃	14500	MPa
80℃	8600	MPa
bending strength
23℃	350	MPa
80℃	250	MPa

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	41	kJ/m²
23℃	43	kJ/m²
Charpy Unnotch Impact strength
-30℃	82	kJ/m²
23℃	96	kJ/m²

THERMAL	Nominal value	Unit
Hot deformation temperature
1.8 MPa, unannealed	242	℃
8.0 MPa, unannealed	217	℃

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	70 to 80	°C
Drying time	2.0 to 4.0	hr
Recommended maximum moisture content	0.15	%
Hopper temperature	70 to 80	°C
Barrel rear temperature	280 to 285	°C
Barrel middle temperature	280 to 290	°C
Barrel front temperature	290 to 300	°C
Nozzle temperature	310 to 320	°C
Processing (melt) temperature	310 to 320	°C
Mold temperature	90 to 120	°C
Injection speed	中等
Back pressure	< 3.00	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.