| About |
|---|
| CYCOLOY CM6140 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) resin is a mineral filled grade, low warpage that can be injection molded. This non-chlorinated, non-brominated flame retardant PC/ABS has a UL V0 & 5VB flame rating. CYCOLOY CM6140 resin is an excellent candidate for a wide variety of thin wall applications including enclosures.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Good liquidity,Halogen free,Flame Characteristics,Heat Resistance, Good |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.26 | g/cm³ | ASTM D792 |
| — | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，2.16kg | 18 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，5 kg | 14.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.50 | % | |
| TD：3.2 mm | 0.40 to 0.60 | % | |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| 24hr，50% RH | 0.010 | % | ASTM D570 |
| Saturation, 23 ℃ | 0.090 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.010 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 3500 | MPa | ASTM D638 |
| — | 3200 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 65.0 | MPa | ASTM D638 |
| yield | 65.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 3.5 | % | ISO 527-2/5 |
| fracture | 100 | % | ASTM D638 |
| fracture | 15 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 3300 | MPa | ASTM D790 |
| — | 3450 | MPa | ISO 178 |
| bending strength | |||
| — | 97.0 | MPa | ISO 178 |
| Yield, 50 mm span | 100 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 10 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 88 | J/m | ASTM D256 |
| 23℃ | 200 | J/m | ASTM D256 |
| -30℃ | 5.0 | kJ/m² | ISO 180-1A |
| 23℃ | 10 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 50.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 97.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 83.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 89.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 80.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 91.0 | ℃ | ASTM D1525 12 |
| B50 | 98.0 | ℃ | ISO 306 |
| B120 | 102 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 5.5E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 6.0E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 6.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.5E+15 | ohms | ASTM D257 |
| Volume resistivity | 2.7E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.60 mm | V-1 | ||
| 0.80 mm | V-0 | ||
| 1.50 mm | 5VB | ||
| Glowing wire flammability index | |||
| 0.80 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 1 mm | 850 | ℃ | |
| 3 mm | 800 | ℃ |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | > 4.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Barrel rear temperature | 275 to 300 | °C | |
| Barrel middle temperature | 275 to 300 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 275 to 300 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. Type I, 0.20 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. at Yield |
| 8. 80*10*3 sp=62mm |
| 9. 80*10*3 mm |
| 10. 80*10*4 mm |
| 11. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |