| About |
|---|
| It is a MDPE compound for solid insulation of telephone singles and data cables at high line speed. It contains a metal deactivator. Applications ME6032 is intended for: Dry core and petroleum jelly filled cables Specifications ME6032 meets the following material classification: ISO 1872-PE, KGHN, 27-D003 ASTM D 1248 Type II, Class A, Category 5, Grade E4, E5 The following cable material standards are met by ME6032: EN 50290-2-23 DIN VDE 0207, 2YI1 DIN VDE 0207, 2YI3 Cables manufactured with ME6032 using sound extrusion practice normally comply with the following cable product standards: IEC 60708 IEC 61156 EN 50288 EN 50407 Special Features ME6032 consists of specially selected components to offer: High extrusion speed up to 2400 m/min Good copper adhesion Excellent surface finish High output&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | MDPE |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,Good bond |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 100% non-ionic surfactant, F20 | > 250 | hr | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 1 second | 53 | ISO 868 | |
| tensile strength | |||
| yield | 17.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 600 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Oxygen sensing time | |||
| 200℃ | 50 | min | IEC 60811-4-2/B |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 2.30 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 1.5E-4 | IEC 60250 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Petroleum jelly absorption | 8.0 | % | IEC 60811-4-2 |
| Heat aging resistance | |||
| 105℃ | > 1.4 | month | IEC 60811-4-2/A |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 165 to 230 | °C | |
| Barrel 2 zone temperature | 165 to 230 | °C | |
| Barrel 3 zone temperature | 165 to 230 | °C | |
| Barrel 4 zone temperature | 165 to 230 | °C | |
| Melt temperature | 220 to 240 | °C | |
| Nozzle temperature | 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |