| High glowing filament and V0 grade flame retardant PA66 Pamphlet: Environmental brominated flame-retardant materials are suitable for electronic components, breaker etc. It is environmental flame-retardant halogen containing nylon material whose flame-retardant grade is VO. And it can pass 750°C hot wire, 30s no burning.&& |
| Product Description | |
|---|---|
| Supplier | Lihan |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,Bromination |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Shrinkage rate | 1.0 to 1.4 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 6.0 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| Melting temperature | 255 to 265 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Glowing wire flammability index | 750 | ℃ | IEC 60695-2-12 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039-2 | |
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2 |
| Bending modulus | 2800 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 60 to 75 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. No Burning |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |