| PBT/PC blend, injection molding grade, non-reinforced, impact modified, excellent toughness at low temperatures, very good paintability&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | High impact resistance,Sprayable,Low temperature toughness |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Specific volume | 1.20 | cm³/g | ASTM D792 |
| Melt Flow Rate | |||
| 250℃，5.0kg | 16 | g/10min | ASTM D1238，ISO 1133 |
| Shrinkage rate | Internal Method | ||
| MD：3.2 mm | 0.80 to 1.0 | % | |
| TD：3.2 mm | 0.80 to 1.0 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 48 | kJ/m² | |
| 23℃ | 63 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -40℃ | 370 | J/m | ASTM D256 |
| -30℃ | 490 | J/m | ASTM D256 |
| -20℃ | 690 | J/m | ASTM D256 |
| -10℃ | 700 | J/m | ASTM D256 |
| 0℃ | 720 | J/m | ASTM D256 |
| 23℃ | 760 | J/m | ASTM D256 |
| -40℃ | 35 | kJ/m² | ISO 180-1A |
| -30℃ | 51 | kJ/m² | ISO 180-1A |
| 23℃ | 63 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 6.4 mm | 115 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 109 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.4 mm | 97.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 90.2 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 123 | ℃ | ASTM D1525, ISO 306/B50, ISO 306/B120 23 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 79 | ISO 868 | |
| Tensile modulus | |||
| — | 1990 | MPa | ASTM D638 |
| — | 2020 | MPa | ASTM D638 |
| — | 2070 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 45.2 | MPa | ASTM D638 |
| yield | 48.8 | MPa | ASTM D638 |
| yield | 52.4 | MPa | ISO 527-2/50 |
| fracture | 46.0 | MPa | ASTM D638 |
| fracture | 47.4 | MPa | ASTM D638 |
| fracture | 50.5 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 4.1 | % | ASTM D638 |
| yield | 4.2 | % | ASTM D638 |
| yield | 4.5 | % | ISO 527-2/50 |
| fracture | 110 | % | ASTM D638 |
| fracture | 120 | % | ASTM D638 |
| fracture | 120 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50 mm span | 1900 | MPa | ASTM D790 |
| — | 2020 | MPa | ISO 178 |
| bending strength | |||
| — | 78.9 | MPa | ISO 178 |
| Yield, 50 mm span | 76.1 | MPa | ASTM D790 |
| Fracture, 50 mm span | 74.7 | MPa | ASTM D790 |
| Fracture bending strain | 7.3 | % | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. Type I, 0.20 in/min |
| 6. 0.051 in/min |
| 7. 0.079 in/min |
| 8. Yield |
| 9. 2 mm/min |
| 10. 80*10*4 sp=62mm |
| 11. 80*10*4 |
| 12. 80*10*4 mm |
| 13. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |