EBAC® SP1806 - SOLIAO

About
Westlake EBAC® SP1806 is an ethylene butyl acrylate copolymer designed for extrusion coating and laminating. SP1806 can also be compounded as an impact modifier or used in highly filled applications. Westlake EBAC® resins are less crystalline and softer than polyethylene and offer compatibility and adhesion to typically difficult to bond to polymers. SP1806 is non-corrosive at extrusion temperatures and has excellent thermal stability.&&

About

Westlake EBAC® SP1806 is an ethylene butyl acrylate copolymer designed for extrusion coating and laminating. SP1806 can also be compounded as an impact modifier or used in highly filled applications. Westlake EBAC® resins are less crystalline and softer than polyethylene and offer compatibility and adhesion to typically difficult to bond to polymers. SP1806 is non-corrosive at extrusion temperatures and has excellent thermal stability.&&

Product Description
Supplier	Westlake Chemical
Generic	EBA
Material Status	Commercial: Active
Features	Good bond,Copolymer,Soft,Heat Stabilized
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.925	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	7.3	g/10min	ASTM D1238
Butyl acrylate composition	17.5	wt%

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	40		ASTM D2240
tensile strength
fracture	10.0	MPa	ASTM D638
Tensile strain
fracture	730	%	ASTM D638

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -73.0	℃	ASTM D746
Vicat Softening Temp	55.0	℃	ASTM D1525
Melting peak temperature	91.0	℃	ASTM D3418

Notes
1. Typical properties: these are not to be construed as specifications.
2. Type IV, 20 in/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.