| H20Z-00 is a nucleated and antistatic polypropylene homopolymer for applications in injection molding, consumer products, housewares, and rigid packaging. This grade has easy moldability, fast cycle times, improved stiffness, and low static charge. This grade has been recognized by UL and meets the requirements of the U.S. Food and Drug Administration specified in 21 CFR 177.1520.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Nucleation,Quick molding cycle,Food contact compliance,Antistatic property,Homopolymer,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.909 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 19 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，Area | 3.27 | kJ/m² | ASTM D256 |
| 23℃ | 33 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 114 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 91 | ASTM D2457 | |
| Haze | |||
| 1270 µm | 68 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 18.7 | MPa | ASTM D638 |
| yield | 37.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 49 | % | ASTM D638 |
| yield | 8.0 | % | ASTM D638 |
| Bending modulus | |||
| 1% secant | 1810 | MPa | ASTM D790-A |
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |