| lution PS 145D offers exceptional processing characteristics for thin walled parts, multi-cavity tools, and complex designs. FEATURES Easy flowing Medium strength APPLICATIONS Artificial jewelry, household articles such as jars and cutlery In high speed high productivity molding applications such as thin walled containers, multicavity small moldings, stationery products like scales etc. Used as a coextruded gloss cap over HIPS Blends with high impact polystyrene Suitable for FFS-sheet&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PS (GPPS) |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent density | 0.60 | g/cm³ | |
| Melt Volume Rate | |||
| 200℃，5 kg | 15.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.60 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | < 0.10 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | < 25 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 88.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 80.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 96.0 | ℃ | ASTM D1525 4 |
| B50 | 88.0 | ℃ | ISO 306 |
| Thermal conductivity coefficient | 0.17 | W/m/K | DIN 52612 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1.5 mm | 140 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 100 Hz | 2.50 | IEC 60250 | |
| 1 MHz | 2.50 | IEC 60250 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 150 | MPa | ISO 2039-1 |
| Tensile modulus | 3300 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 44.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2 |
| bending strength | 70.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 280 | °C | |
| Mold temperature | 10 to 60 | °C | |
| Injection Velocity | 200 | mm/sec | |
| Melt temperature | < 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. with external lubricant |
| 3. 4h/80°C |
| 4. Rate B (120°C/h), Loading 1 (10 N) |
| 5. Short Time |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |